Dental resins for LCD and DLP printers
The model and the crown, from the same printer.
X print for dental models. X perm for permanent crowns and bridges. Each resin has its own data sheet and print settings below.
- mm
- Layer height, both resins
- g/cm³
- Density, both resins
- months
- Shelf life, both resins
- °C
- Storage, both resins
Dental model resin · 1 kg · 8K series
Stiff enough to trust the margin.
A model resin with a flexural modulus of 1699.7 MPa and a hardness of 80–88 Shore D.
Want to sell X print and X perm in your market? Become a dealer
MPa
Flexural modulus
MPa
Flexural strength
J/m
Notched impact strength
Mechanical, after curing
- Flexural modulus
- 1699.7 MPa
- Flexural strength
- 57.91 MPa
- Tensile strength
- 37.88 MPa
- Tensile modulus
- 615.49 MPa
- Notched impact strength
- 72 J/m
- Maximum force
- 160.7 KGF
- Elongation at yield
- 3.09 %
- Elongation at break
- 6.41 %
- Hardness
- 80–88 Shore D
Print settings
- Layer height
- 0.05 mm
- Bottom exposure
- 25–35 s
- Layer exposure
- 2.5–3.5 s
- Bottom lift distance
- 6 mm
- Lifting distance
- 6 mm
- Bottom lift speed
- 60 mm/min
- Lifting speed
- 80 mm/min
- Retract speed
- 150 mm/min
Liquid and storage
- Viscosity
- 250–400 mPa·s
- Density
- 1.05–1.25 g/cm³
- Net weight
- 1 kg
- Shelf life
- 24 months
- Storage
- 25–30 °C
- Shake the resin well before use.
- Seal after use; store dry, ventilated and out of the sun.
- Wear protective gloves, mask and clothing when handling.
Lifting distance by screen size
FEP / nFEP film
- 6 mm
- under 7″
- 8–10 mm
- 7–10″
- 11 mm
- 10.1″
- 14 mm
- 13.3″
- 15 mm
- 15″
Settings were tested on a 6.6″ monochrome LCD at 3500–4500 µW/cm²; adjust them for your printer and model. With ACF film, lifting distance can be reduced by 30–50%. If your printer's light output weakens and prints fail, increase exposure time.
Permanent crown and bridge resin · LT series
A printed crown that stays in.
For permanent crowns and bridges. High hardness, good toughness and wear resistance, low water absorption and low shrinkage, with high precision and dimensional stability.
- Crowns
- Bridges
Want to sell X print and X perm in your market? Become a dealer
MPa
Flexural strength
MPa
Tensile strength
°C
Heat deflection temperature
Mechanical, after curing
- Flexural strength
- 68.91 MPa
- Flexural modulus
- 1866.83 MPa
- Tensile strength
- 53.87 MPa
- Tensile modulus
- 678.64 MPa
- Impact strength
- 37.35 J/m
- Maximum force
- 228.55 KGF
- Elongation at yield
- 6.36 %
- Elongation at break
- 17.68 %
- Hardness
- 81–87 Shore D
- Heat deflection temperature
- 79.72 °C
Print settings
- Layer height
- 0.05 / 0.025 mm
- Bottom exposure
- 20–30 s
- Layer exposure
- 3–4 s
- Bottom lift distance
- 6 mm
- Lifting distance
- 6 mm
- Bottom lift speed
- 60 mm/min
- Lifting speed
- 80 mm/min
- Retract speed
- 150 mm/min
- Wavelength
- 385–410 nm
Liquid and storage
- Viscosity
- 850–1000 mPa·s
- Density
- 1.05–1.25 g/cm³
- Shelf life
- 24 months
- Storage
- 25–30 °C
- Single use: the resin cannot be reused.
- Seal immediately after use; store dry, ventilated and out of the sun.
- Use with good ventilation and wear a mask; avoid contact with eyes and skin.
Print settings are for a 6.6″ monochrome screen at 3500–4500 µW/cm².
Side by side
Which resin for which job.
X print for models. X perm for crowns and bridges.
| Parameter | X print — models | X perm — crowns, bridges |
|---|---|---|
| Flexural strength | 57.91 MPa | 68.91 MPa |
| Flexural modulus | 1699.7 MPa | 1866.83 MPa |
| Tensile strength | 37.88 MPa | 53.87 MPa |
| Impact strength | 72 J/m | 37.35 J/m |
| Elongation at break | 6.41 % | 17.68 % |
| Hardness | 80–88 Shore D | 81–87 Shore D |
| Viscosity | 250–400 mPa·s | 850–1000 mPa·s |
| Bottom exposure | 25–35 s | 20–30 s |
| Layer exposure | 2.5–3.5 s | 3–4 s |
Next step
Order the X range online.
Clinics and laboratories buy directly in our online shop. Want to sell the range in your market? Apply to become a dealer.